Property | Test Method | Test Results | Notes |
Abrasion Resistance | ASTM D4060-10 | 33mg (1000 cycles) |
|
Brinell Hardness | EN15534 | 8.2N/mm2 |
|
Boiling Test | EN15534 | Water absorption in weight: 1.1% |
|
Bond Strength | EN319 | Average Bond strength > 2.3MPa No obvious abruption and damage after test |
|
Coefficient Linear Thermal Expansion | ASTM D696 EN15534 | 38.9×10-8mm/mmc 32.2×10-6 K-1 |
|
Creep Behaviour | EN15534 | △S:4.70mm, △Sr:2.91mm | Span:400mm |
Content of Pentachlorophenol | CE (EN14041(2004)) | 2.99ppm |
|
Creep Recovery | ASTM D7032 | Creep recovery after 24h: 93% |
|
Degree of Chalking | EN15534 | Rating 0, no chalking |
|
Electrostatic Behaviour | EN1815 | Body-Voltage: 1.1kV This floor covering can be classified as anti-static. |
|
Fire Resistance | BS476-7
EN13501-1, EN ISO9239-1, EN ISO11925-2
GB8624, GB11785 GB8626, GB20286
ASTM E84 | Class 2
Reaction to fire classification Bfl-S1
Reaction to fire classification GB8624B1(B-S1, T1) Flame Spread Index (FSI): 85 Smoke Developed Index (SDI): 300
| On Request please advise when speaking to seller |
Falling Mass Impact Resistance | EN15634 | Max Crack Length (mm): no crack Max Residual Indentation (mm): 0.14 |
|
Formaldehyde Content | EN717-1 ASTM D6007-14 | Non-Detected Non Detected |
|
Flexural Properties | EN15534
ASTM D6109 | Bending Strength: 26.2Mpa, Modulus of Elasticity: 3.10Gpa, Maximum Load 4537N Deflection at 500N; 0.88mm
MOR:24.8MPa, MOE:3495MPa | Span:400mm |
Heavy Metal Content | EPA3052 | Sb:ND, As:ND, Se:ND, Sn:ND |
|
Heat Reversion | EN15534 EN 479 | Test temperature: 100c: 017% |
|
Heat Build-up | EN15534 | △t=-2.7c |
|
Impact Resistance | ASTM D4226 | MFE>396J |
|
Lead Content Test | EUNo.628/2015 | Non Derectable |
|
Mould Resistance | ASTM G21 | Rating: 0 |
|
Moisture Content | EN15534, EN322 | 0.83% |
|
Moisture Resistance Under Cyclic Test Conditions | EN15534 | Original MOR: 27.4mPA After exposure, MOR24.8Mpa, Decrease: 9.6%, |
|
Neutral Salt Spray Test | ASTM B117-2011
EN15534, ISO9227 | After 200 hour test, there was no visible change appeared on the surface: Front surface: △E *=1.22, grey scale; 4-5 Back surface: △E *=1.06 grey scale; 4-5
△E *=1.42, grey scale; 4 (Exposure 96h) |
|
pb, cd, hg, cr5+ | RoHs-IEC62321 5+ | pb:ND, cd:ND, hg:ND, cr5+:ND |
|
Resistance to Scratch Test | ISO4586-2 | Rate 2 |
|
Resistance to Indentation | EN15534 | Apply 2000N load Brinell hardness: 72Mpa, Rate of elastic recovery 65% |
|
Resistance to Artificial Weathering | EN15534 ISO4892-2 | After 2000h exposure △E*=1.09, grey scale=4-5 |
|
Rockwell Hardness | ASTM D785 | 78.7R |
|
Slip Resistance | PVT BS 7676-2:2002 (Four S/Slider 96) (TRL/Slider 55) | Wide groove (dry) PVT 82, wood grain (dry) PVT 83, wide groove (wet) PTV 34, wood grain (wet) PTV 38 | For commercial application 1 person in 10,000 requires a PTV of 34 for safety. |
Swelling & Water Absorption (24 hours submersion) | EN15534 | 1 Swelling: 0.06% in thickness, 0.03% in width, 0.03% in length 2 Water absorption: 0.49% |
|
Swelling & Water Absorption (28 days submersion) | EN15534 | 1 Swelling: 0.78% in thickness, 0.07% in width, 0.12% in length 2 Water absorption: 1.66% |
|
SRI Testing | ASTM C1549 ASTM C1371 ASTM E1980 | 19 |
|
Surface Bond Quality | EN319 | >2.08Mpa |
|
Thermal Resistance | ASTM C518-2010 | Thermal Conductivity: 03589W/(m-k) Thermal Resistance: 0.0830(m2-k)/W |
|
Thermal Conductivity | CE (EN14041(2004)) | 0.19738W/(m-k) |
|
UV Weathering Test | ASTM G154 | After 3000 hour test grey scale3, △E*=3.56 |
|
Uplift Resistance | ICC-ES AC174 ASTM E330 | Average ultimate load ≥427psf |
|
VOC & TVOC | ASTM D5116-11 | Non Detectable |
|